Sviluppo di materiali innovativi per adsorbimento H2 e realizzazione di una unità dimostrativa di bombola
Mostra/ Apri
Creato da
Pedicini, Rolando
Cipparrone, Gabriella
Agostino, Raffaele Giuseppe
Metadata
Mostra tutti i dati dell'itemDescrizione
Formato
/
UNIVERSITA’ DELLA CALABRIA
Dipartimento di Fisica
Dottorato di Ricerca in
Scienze e Tecnologie Fisiche, Chimiche e dei Materiali
Ciclo XXXII; The research activity carried out during this three-year of PhD was directed towards the synthesis
of new materials for the hydrogen storage. In particular, the PEEK was used as a basic polymeric
matrix; this is an aromatic polymer, heat-resistant of which many properties are known. This base
material does not show such chemical-physical characteristics that it can be used to bind and release
H2 molecules, moreover, not being a porous material, cannot even think of a physical bond with H2.
A functionalization reaction was necessary in which a certain percentage of chlorosulfonic groups
on the aromatic ring of the polymer was introduced. This reaction resulted in both a slight increase
in the surface area (from 9 to 19 m2/g) and also a morphological variation of the material was
observed. To give the possibility to hydrogen to bind, presumably in a chemical way to the polymer,
the chloride was exchanged with the permanganate ion, coming from a solution of KMnO4, that act
like a precursor, which in an acidic environment is reduced to MnO2. The importance of the synthesis
parameters such as time and temperature and the concentration of the precursor was verified.
From the study of these parameters, different materials have been synthesized with a metal oxide
load ranging from 7 to 80 wt%. The X-ray study showed that the Mn oxide synthesised is of the
Birnessite type, having a characteristic lamellar structure, needle-like structure with characteristic
peaks located at 2q = 12 °, 37 ° and 66 °. It was found that the increase in the percentage of oxide
in the composite material is almost directly proportional to the absorption capacity. From
absorption measurements by Sievert apparatus at 110 °C / 60bar, particularly interesting results
were obtained, reaching 1 wt% of H2 absorption with materials having a load of 80 wt% of Mn oxide.
It has been seen how the increase of the synthesis temperature at 80 °C and 95 °C does not involve
any variation from the H2 adsorption but changes, probably, the structure of the oxide clusters
which tend to be smaller in size. Moreover, from post volumetric measurement analysis, evident
differences were found, in fact the initial MnO2 (IV) was reduced in Mn2O3 (III). For this reason, the
synthesis temperature was decreased to 50 °C, reducing the analysis temperature from 110 °C to
50 °C by operating at 40 bars, in these conditions, over 3 wt% of H2 absorption was revealed,
moreover, a reversible trend after three cycles of abs / des was obtained. These results seem to
suggest a chemical interaction between hydrogen and the material. This material was then selected
as an absorbent material to be introduced into a laboratory prototype tank (having a volume of 20L)
that powered a 10W fuel cell. After increasing the material synthesis from 2 to 10 g, leaving all the
chemical-physical and H2 absorption properties unaltered, the tank was designed considering some
of the basic characteristics of the material. To characterize the tank two tests were designed: an
electrochemical one in which the prototype was directly connected to the tank and the cell power
and its life in real time was followed. Through this test, a power system had achieved a value of
about 10W for an average time of 6min, less than the expected time of 20min, due to H2 losses in
the tank / cell system. This problem was also recorded using the other method through mass flow
and P sensors at the inlet and outlet of the tank. Considering that the system is a small
demonstration developed on a laboratory scale and the components used were probably unsuitable
for this purpose, by making the necessary changes and shrewdness, the H2 losses can be eliminated
and, consequently, the life of the tank can reach the ideal value.Soggetto
Sintesi dei materiali compositi; Stoccaggio H2; Caratterizzazioni chimico-fisiche